Size [Inch] |
As supplied [mm] |
After Recovery [mm] |
Lomex cikkszám |
||
Min ID |
Wall- thickness |
Max ID |
Wall- thickness |
||
3/64 |
1.2 |
0.18 ± 0.05 |
≤ 0.6 |
0.30 ± 0.05 |
|
1/16 |
1.6 |
0.18 ± 0.05 |
≤ 0.8 |
0.32 ± 0.05 |
|
3/32 |
2.4 |
0.18 ± 0.05 |
≤ 1.00 |
0.35 ± 0.05 |
|
1/8 |
3.2 |
0.20 ± 0.05 |
≤ 1.5 |
0.38 ± 0.05 |
|
3/16 |
4.8 |
0.23 ± 0.05 |
≤ 2.0 |
0.45 ± 0.05 |
|
1/4 |
6.4 |
0.25 ± 0.05 |
≤ 3.0 |
0.50 ± 0.05 |
|
3/8 |
9.5 |
0.30 ± 0.08 |
≤ 4.5 |
0.60 ± 0.08 |
|
1/2 |
12.7 |
0.30 ± 0.08 |
≤ 6.0 |
0.60 ± 0.08 |
|
3/4 |
19.1 |
0.40 ± 0.12 |
≤ 10.0 |
0.75 ± 0.12 |
|
1 |
25.4 |
0.45 ± 0.12 |
≤ 12.5 |
0.90 ± 0.12 |
|
1 - 1/4 |
31.8 |
0.45 ± 0.12 |
≤ 15.0 |
0.90 ± 0.12 |
|
1 - 1/2 |
38.1 |
0.50 ± 0.15 |
≤ 21 |
1.00 ± 0.30 |
|
2 |
50.8 |
0.50 ± 0.15 |
≤27 |
1.00 ± 0.30 |
|
| Shrink Temperature [°C] | 90 | |
| Temperature Range [°C] | 125 | |
| Radial Shrinking Ratio [%] | ≥ 50 | |
| Longitudinal Change [%] | ≤ 5 | |
| Tensile Strength [Mpa] | ≥ 10.4 | |
| Ultimate Elongation [%] | ≥ 200 | |
| Aging in Circulating-air Oven | 158.0 ± 1.0°C, 168hrs | |
| After aging | Tensile Strength [Mpa] | ≥ 7.3 |
| Ultimate Elongation [%] | ≥ 100 | |
| Volume Resistivity [Ω cm] | ≥ 1014 | |
| Dielectric Strength at 1 min, AC2500V | No breakdown | |
| Flammability | VW-1 | |
| Concentricity [%] | ≥ 65 |
Tulajdonságok: |
|
Széleskörűen használható elektronikus alkalmazások területén, mint például autóipar, repülőgépipar, építőipar, tömegközlekedési járművek
Felhasználható speciális alakú tárgyak védelmére, jelölésére, mint például vezetékek végződéseinek illetve elektromos csatlakozások szigetelésére
Jó mechanikai szilárdság jellemzi, védelmet nyújt nedvesség, folyadékok és korrózió ellen, de használják csatlakozó és vezeték közös szigetelésére is